CNTE
Pure carbon nanotubes exhibit superlubricity  approximately ZERO friction between neighboring tubes in a bundle. In 2013, Zhang et. al. published a paper on carbon nanotube superlubricity that measured the intershell sliding force of a 1 centimeter doublewall carbon nanotube (DWCNT). Three diameters were measured, and the tiny pullout force matched theory, pa function of outer tube diameter.
Zhang et. al. 

Laurent et. al 

Diameter 
Pullout 

Inner 
Density 
Tubes 
Pullout 
Strength 
nm 
Force nN 

nm 
Kg/m³ 
/ m² 
Pressure 
Kyuri 
2.73 
1.37 

2.39 
1951 
1.16e17 
159 MPa 
81.5 
2.93 
1.47 

2.59 
1835 
1.01e17 
148 MPa 
80.7 
3.26 
1.64 

2.92 
1672 
8.10e16 
134 MPa 
80.1 
Laurent et. al. estimates that the inner tube diameter is 0.34 nM ( d_{ss} ) less than the outer tube diameter, and that DWCNT density (g/cm³) is:
d_{MW} = 6084 { \Large { ( d_{out} ~  ~ d_{ss} ) \over { d_{out}^2 } } } with d_{out} and d_{ss} in nanometers.
I added my own estimations for perfect hexagonally close packed tube density, Tubes/m² = \sqrt( 3 ) / 2 D^2 = 0.866 / D^2 The pullout pressure P = 866 F / D^2 mPa if F is nanonewtons and D is nanometers. Results:
Zhang et. al. 

Laurent et. al 

Diameter 
Pullout 

Inner 
Density 
Tubes 
Pullout 
Strength 
nm 
Force nN 

nm 
kg/m³ 
/ m² 
Pressure 
Kyuri 
2.73 
1.37 

2.39 
1951 
1.16e17 
159 MPa 
81.5 
2.93 
1.47 

2.59 
1835 
1.01e17 
148 MPa 
80.7 
3.26 
1.64 

2.92 
1672 
8.10e16 
134 MPa 
80.1 
These strengths for pure, perfect DWCNT are less than 0.2% of the minimum strength needed for a space elevator, and 2% of the strength of Torayca 1100G carbon fiber. Furthermore, given these pullout forces, which will be unevenly distributed in real atomically imperfect materials, the stretch will not recover; these are not spring forces, but disassembly forces. After the material slides apart, it will not go back together, the hysteresis is unity. This is weak taffy, not a strong elastic material like kevlar or carbon fiber, or even a .
The situation is grim but not completely hopeless. In CNT fibers  yarns between the extremes, Dr. Thurid Gspann et. al. suggests that defects create loadsharing crosslinks between tubes, but can reduce strength from the theoretical 100 GPa by 30% to 70%. Even with the theoretical "best defect" maximum of 70 GPa, and a density of 1700 kg/m, this theoretical atomicprecision macromaterial will have a strength of 41 Myuri, less than the 48 Myuri (derated by 40% to 34 Myuri) material assumed by the 2013 Space Elevators assessment.
If ≈ 40 Myuri is potentially possible with perfect "precisiondefect" CNT (based on current pessimistic knowledge), there may be an atomicallyperfect 3D material structure with zero hysteresis and 40 Myuri strength. May be; in 2017, we do not have a scintilla of a clue how to do that. Indeed, these may be selfrepairing pseudolifelike complex nanostructures that can repair and grow themselves under tension, but are far beyond our current understanding and technological imagination.
Space elevators have assumed diamondlike crystal tethers since the 1970s, and carbon nanotube tethers since the 1990s. The materials necessary have not yet been discovered, or even imagined in practical detail.